High-Load Bearing O-Ring for Sealing Between Metal Plates

• Customization: Available
• Material: NBR
• Application: Seal
• Model NO.: OR39
• Type: Mold Compression
• Performance: Temperature
• Shape: O-Ring
• Standard: Standard
• Temperature: -30- to 150c
• Tensile Strength: 8 MPa
• Compression Set 22h 175c: 25
• OEM/ODM: Avaialable
• Elogation at Break: Min 290%
• Hardness: 40-90 Shore
• Special Request: Physical and Chemical Properties
• Sample: Free
• Color: Black, Red, Blue, Brown, White, or Others
• Price Term: Fob, CIF, CNF, EXW
• Transport Package: Bag and Carton
• Specification: All sizes
• Origin: Jiangsu, China
• HS Code: 4016931000
• Production Capacity: 300000000PCS/Month
• Package Size: 20.00cm * 20.00cm * 20.00cm
• Package Gross Weight: 1.000kg

Product Description

Different sizes and material oring o ring o-ring nbr fkm silicone epdm materials.

In designing an O-ring Seal, it is best to determine the O-ring compound first, as the selected compound may have significant influence on gland design parameters. Essentially, the application determines the rubber compound; The primary factor being the fluid to be sealed. The elastomer however, must also resist extrusion when exposed to the maximum anticipated system pressure and be capable of maintaining good physical properties through the full temperature range expected. In dynamic applications, the selected material must also have the toughness and abrasion resistance so important in reciprocating and rotary seals. Essentially, the application determines the rubber compound; The primary factor being the fluid to be sealed. The elastomer however, must also resist extrusion when exposed to the maximum anticipated system pressure and be capable of maintaining good physical properties through the full temperature range expected. In dynamic applications, the selected material must also have the toughness and abrasion resistance so important in reciprocating and rotary seals.

Product Description

Material-NBR

NBR o-rings also referred to as NBR o-rings and Nitrile o-rings are the most widely used o-ring material in the world because of low cost, good mechanical performance with resistance to water, most basic oils, lubricants and some fuels, many pneumatic, hydraulic systems, and the default choice for basic applications. The Buna-N O-rings have good abrasion resistance, tensile strength and compression set resistance.

Due to its excellent resistance to petroleum products, and its ability to be compounded for service over a temperature range of -35°C to +120°C (-30°F to +250°F), Nitrile /NBR is the most widely used elastomer in the seal industry today. Also many  rubber specifications for fuel and oil resistant O-rings require nitrile based compounds.

Temperature Range: NBR / Nitrile O-Rings resists oil-based hydraulic fluids, fats and oils. Temperature Range -30°C to+120°C with Durometer/Hardness 70.

Specification

Material-EPDM

EPDM O-Rings are also referred to as ethylene-propylene o-rings because of the chemical composition of the same name. The use of EPDM o-rings and seals are commonly found in the automotive manufacturing industry where sealing of brake systems is required. EPDM material is also compatible with heat as in steam and water vapor. EPDM o-rings have great flexibility and chemical resistance at low temperatures. resistance to ozone, sunlight, and weathering and have great flexibility and chemical resistance at low temperatures. 

Temperature Range: For EPDM the service temperature can be designed from -55° C to 125° C or up to 150° C (for peroxide cured systems).

List of O-ring standards
Standard	O-ring Cross-sectional Diameter (W)
AS 568 BS 1516	1.78	2.62	3.53	5.33	6.99
JISB2401	1.9	2.4	3.1	3.5	5.7	8.4
ISO 3601/1 DIN 3771/1 GB 3452.1	1.8	2.65	3.55	5.3	7
Preferred metric size	1	1.5	2	2.5	3
	3.5	4	4.5	5	5.5
	6	7	8	10	12
AS 568 (900 series)	1.02	1.42	1.63	1.83	1.98
	2.08	2.21	2.46	2.95	3

Performance parameters
	Static Seal	Dynamic Seal
Working pressure	Up to 20 MPa without a back-up ring;	Up to 5 MPa without a back-up ring;
	Up to 40 MPa with a back-up ring;	Higher pressure with a back-up ring.
	Up to 200 MPa with a special back-up ring.
Movement speed	The maximum reciprocating speed can reach 0.5 m/s and the maximum rotating speed can reach 2.0 m/s.
Temperature	General applications:-30°C~+110°C;special rubber:-60°C~+250°C;rotating applications:-30°C~+80°C
Medium	See Raw Material Characteristics of Rubber Seals

NBR 70 PHYSICAL TEST REPORT
Materia: NBR70-20           Standard:ASTM D2000 M2BG710A14B14E014E034EA14EF11EF21
Press cure:sheet 170℃ 6min Button:170℃ 8min                 Post Cure:Sheet 120℃ 2h Button:120℃ 2h
Test Item		Test Condition	Standards	Test result
Test under normal situation	Hardness(Shore-A)	Room temperature	70±5	70
	Tensile strength(Mpa)		≥10	14
	Elongation (%)		≥250	314
	Density(g/cm3)		/	1.215
Aging-Resistanc e Testing	Hardness Change(Shore-A)	100℃×70 h	≤+15	5
	Tensile strength Change(%)		≤-20	4
	Elongation Change(%)		≤−40	−21.5
Compression set	Compression set(%)	100℃×22h	≤25	8.1
Oil-Resistance No.1 OIL	Hardness Change(Shore-A)	100°C × 70 h	≤-5~+10	8
	Tensile strength Change(%)		≤-25	9
	Elongation Change(%)		≤-45	-9.7
	Volume Change(%)		-10~+5	-9.5
Oil-Resistance N0.3 OIL	Hardness Change(Shore-A)	100℃×70 h	-10~+5	-1
	Tensile strength Change(%)		≤-45	6.6
	Elongation Change(%)		≤-45	-2.3
	Volume Change(%)		0~+25	5.3
Water Resistance	Hardness Change(Shore-A)	100℃×70 h	±10	-2
	Volume Change(%)		±15	3.6

EPDM 70 PHYSICAL TEST REPORT
Material: EPDM70              Standard:ASTM D2000 M2AA707A13B13
Press cure:sheet 170℃ 10min Button:170℃ 15min             Post cure:sheet 120℃ 2H Button:120℃ 2H
Test Item		Test Condition	Standards	Test result
Original Properties	Hardness(Shore-A)	23℃	70±5	72
	Tensile strength(MPA)		≥10	13.8
	Elongation (%)		≥200	310
	Density(g/cm3)		/	1.14
Aging-Resistanc e Testing	Hardness Change(Shore-A)	70℃×70 h	≤+15	2
	Tensile strength Change(%)		±30	1.2
	Elongation Change(%)		≤−50	-5.6
Compression set	Compression set(%)	70℃×22 h	≤25	16.5
Conclusion test:OK

Company Profile

Suzhou ARISONS New Material Co.,Ltd.

ARISONS is a professional Rubber&Construction manufacturer in China. The factory is located in Jiangsu, closed to Shanghai. After 15 years of development, it has a mature production system, a professional engineering team, a quality inspection department and a strong production line, providing a one-stop design scheme and product design for customers in many countries.

Our main products are rubber sealing products, pipe sealing ring, car sealing ring, etc., water treatment equipment, aeration pipe, aeration disk, large pipe machine, driving, etc., we pay attention to quality, and will make different solutions according to different customers, provide the cheapest price, achieve the most perfect effect, has reached more partners for customers, look forward to cooperation with you!

FAQ

Q1. What is your terms of packing?
A: Generally, we pack our goods in Blank Cartons. We privode carton LOGO print service after getting your authorization letters.

Q2. What is your terms of payment?
A: T/T 30% as deposit, and 70% before after receive the copy of B/L. We'll show you the photos of the products and packages before you pay the balance.

Q3. What is your terms of delivery?
A: We accept FOB,CIF,CNF,DDP,DDU,LC.etc

Q4. How about your delivery time?
A: Generally, it will take 7 to 10 days after receiving your advance payment. The specific delivery time depends on the items and the quantity of your order.

Q5. Can you produce according to the samples?
A: Yes, we can produce by your samples or technical drawings.

Q6. What is your sample policy?
A: We can supply the sample for free, client only need to pay the delivery cost.